C36500, also known as Leaded Muntz Metal or CW610N, is a brass alloy known for its excellent machinability, good corrosion resistance, and moderate strength. It is copper alloyed primarily with zinc, tin, and lead, making it suitable for a wide range of applications, including condensers, evaporators, tubesheets, heat exchangers, fasteners, and architectural components.
Chemical Composition
Copper (Cu): 58.00 – 61.00%
Lead (Pb): 0.25 – 0.70%
Tin (Sn): 0.25 – 1.00%
Iron (Fe): Up to 0.15%
Zinc (Zn): Remainder (Balance)
Mechanical Properties
Tensile Strength: Approximately 400 – 500 MPa
Yield Strength: Approximately 160 – 320 MPa
Elongation: About 30 – 40%
Hardness: Approximately 75 Rockwell F scale
Physical Properties
Density: 8.41 g/cm³
Electrical Conductivity: Approximately 28% IACS at 68°F