CW717R is a naval brass alloy known for its high ductility, excellent electrical and thermal conductivity, strong impact resistance, good creep resistance, and ease of welding. It also has low volatility under high vacuum.
Chemical Composition
Copper (Cu): 59.00 – 62.00%
Tin (Sn): 0.50 – 1.00%
Arsenic (As): 0.02 – 0.06%
Lead (Pb): Up to 0.20%
Iron (Fe): Up to 0.10%
Nickel (Ni): Up to 0.20%
Zinc (Zn): Balance
Total others: Up to 0.20%
Mechanical Properties (As per temper R320)
Tensile Strength (UTS): Minimum 320 MPa
Proof Stress (PS): Minimum 100 MPa
Elongation: Minimum 30%
Hardness: Varies depending on shape and form
Physical Properties
Melting Point: Solidus ~1630°F, Liquidus ~1650°F
Density: 8.41 g/cm³ (0.304 lb/cu in at 68°F)
Electrical Conductivity: 26% IACS at 68°F
Thermal Conductivity: 67 BTU/(ft²·hr·°F)
Coefficient of Thermal Expansion: 11.8 × 10⁻⁶ per °F
Modulus of Elasticity: 15000 ksi
Modulus of Rigidity: 5600 ksi
Fabrication Properties
Excellent soldering and brazing
Good oxyacetylene welding
Fair gas shielded arc welding
Not recommended for coated metal arc welding
Good spot and butt welding
Fair cold workability and excellent hot workability